Resumen de Chromium adsorption from tannery effluents by activated carbons prepared from coconut shells by chemical activation with koh and zncl2

S. Bendezú, J. Oyague, A. Romero, R García, Y. Muñoz, N. Escalon

• español

  Se prepararon carbones activados de elevadas propiedades adsorbentes desde cáscaras de coco mediante activación química usando como agentes activantes el KOH y ZnCL2, en atmósfera de N2(g) y CO2(g), respectivamente, para adsorber especies de cromo desde soluciones acuosas y efluentes de Curtiembres. Se halló que la capacidad de adsorción de los carbones activados obtenidos es significativamente mayor que el carbón comercial usado. En base a resultados obtenidos de los diversos métodos de caracterización, se determinó la presencia de grupos funcionales orgánicos, fenoles y carbonilos, responsables de la carga superficial de los carbones activados que favoreció la adsorción de las especies de cromo, medidas de potencial zeta ayudaron a explicar la adsorción del metal en términos de la acción electrostática atracción-repulsión de la superficie del carbón activado y los cationes Cr(III) y oxianiones Cr(VI), respectivamente. Se observó que los carbones activados CK12 y CZ32 muestran las propiedades adsorbentes más altas, se adsorbió aproximadamente 721,38 mg de cromo con el CK12, 534,43 mg con el CZ32 y solamente 274,02 mg con el carbón comercial (CC), por gramo de carbón activado, respectivamente, a pH 4,45 desde los efluentes de Curtiembres

• English

  Activated carbons of high adsorbents properties for adsorption of chromium species from aqueous solution and Tannery effluents were prepared from coconut shells by means of chemical activation using as activating agents the KOH and ZnCL2, in atmosphere of N2(g) and CO2(g), respectively. It was found that the adsorption capacity of the produced activated carbons are significantly higher than that of the commercial one that was tested. Based on the results obtained from a variety of characterization methods, it has been determined the presence of functional organic groups, phenols and carbonyls, which are responsible for the activated carbons surface charge and it favored the chromium species adsorption, zeta potential measurements helped to explain the metal adsorption in terms of electrostatic attraction-repulsion behavior of the activated carbon surface and cations of Cr(III) and oxyanions of Cr(VI), respectively. It was observed that the activated carbons CK12 and CZ32 displayed the biggest adsorbents properties, it was adsorbed approximately 721.38 mg of chromium with the CK12, 534.43 mg with the CZ32, and only 274.02 mg with the commercial carbon (CC), by gram of activated carbon, respectively, at pH 4.45 from Tannery effluents