Estudio in vitro: Microfiltración marginal en restauraciones con resina compuesta clase II

• Calizaya-Bendita, Danny ^[1] ; Chávez-Fernández , Fernando ; Loaiza-Jara, Lizeth ^[1] ; Molina-Arraya, Evelyn ^[1] ; Mamani-Cori, Vilma ^[1] ; Poma, Ronald ^[1]
  1. [1] Universidad Nacional del Altiplano
• Localización: Revista Acciones Médicas, ISSN-e 2955-8026, Vol. 2, Nº. 1, 2023, págs. 24-31
• Idioma: español
• Títulos paralelos:
  • Estudo in vitro: microinfiltração marginal em restaurações com resina composta classe II
  • In vitro study: Marginal microleakage in restorations with class II composite resin
• Enlaces
  • Texto completo
• Resumen
  • español

    Objetivo: evaluar in vitro la microfiltración marginal en restauraciones con resina compuesta clase II en dientes posteriores. Método: Se realizó un estudio de diseño cuasiexperimental de corte longitudinal, la muestra estuvo conformada por 40 dientes posteriores superiores e inferiores (premolares y molares) sanos, estos fueron extraídos por indicaciones ortodónticas o periodónticas y se han conservado en agua destilada por 48 horas; se excluyeron aquellos dientes que tenían restauraciones oclusales o alguna alteración de forma o estructura. Los dientes fueron distribuidos aleatoriamente en 02 grupos experimentales. El grupo experimental 1 (GE1) recibió la restauración con resina compuesta clase II con base ionomérica y el grupo experimental 2 (GE2) recibió la restauración con resina compuesta clase II sin base ionomérica. Resultados: al comparar el grado de microfiltración marginal entre el GE1 y GE2 a las 48 horas, 15 días, 30 días y 45 días con un nivel de confianza de 95% existe diferencia estadísticamente significativa (p < 0,05), es decir que, existe un mayor grado de microfiltración marginal en restauraciones con resina compuesta clase II sin base ionomérica. Conclusión: Las restauraciones con resina compuesta clase II en dientes posteriores que no tuvieron una base ionomérica tienen mayor grado de microfiltración marginal.

  • English

    Objective: to evaluate in vitro marginal microleakage in class II composite resin restorations in posterior teeth. Method: A quasi-experimental design study of longitudinal section was carried out, the sample consisted of 40 healthy upper and lower posterior teeth (premolars and molars), these were extracted for orthodontic or periodontal indications and have been preserved in distilled water for 48 hours; Those teeth that had occlusal restorations or any alteration in shape or structure were excluded. The teeth were randomly distributed in 02 experimental groups. Experimental group 1 (GE1) received the restoration with class II composite resin with ionomer base and experimental group 2 (GE2) received the restoration with class II composite resin without ionomer base. Results: when comparing the degree of marginal microleakage between GE1 and GE2 at 48 hours, 15 days, 30 days and 45 days with a confidence level of 95%, there is a statistically significant difference (p < 0.05), that is to say that, there is a higher degree of marginal microleakage in restorations with class II composite resin without ionomer base. Conclusion: Class II composite resin restorations in posterior teeth that did not have an ionomeric base have a higher degree of marginal microleakage.

  • português

    Objetivo: avaliar in vitro a microinfiltração marginal em restaurações de resina composta classe II em dentes posteriores. Método: Foi realizado um estudo de desenho quase experimental de corte longitudinal, a amostra foi composta por 40 dentes posteriores superiores e inferiores hígidos (pré-molares e molares), estes foram extraídos por indicações ortodônticas ou periodontais e foram preservados em água destilada por 48 horas; Foram excluídos os dentes que apresentavam restaurações oclusais ou qualquer alteração na forma ou estrutura. Os dentes foram distribuídos aleatoriamente em 02 grupos experimentais. O grupo experimental 1 (GE1) recebeu a restauração com resina composta classe II com base de ionômero e o grupo experimental 2 (GE2) recebeu a restauração com resina composta classe II sem base de ionômero. Resultados: ao comparar o grau de microinfiltração marginal entre GE1 e GE2 às 48 horas, 15 dias, 30 dias e 45 dias com nível de confiança de 95%, há diferença estatisticamente significante (p < 0,05), ou seja, há maior grau de microinfiltração marginal em restaurações com resina composta classe II sem base ionomérica. Conclusão: Restaurações de resina composta Classe II em dentes posteriores que não possuíam base ionomérica apresentam maior grau de microinfiltração marginal.