Resumen de Mechanical evaluation for three-dimensional printed orthodontic springs with different heights-in vitro study
Dragan Ströbele, Ahmed Othman, Vasilios Alevizakos, Mesut Turan, Constantin von See
Background: The orthodontic spring materials in use have a significant influence on the applied forces. The prerequisite to identify the in vitro force deflection of the CAD/CAM fabricated springs is considered mandatory to identify the material characteristics. The purpose of the present investigation was to evaluate the mechanical load on 3D printed springs using different coil heights.
Material and Methods: The springs were digitally designed with different coil heights using Autodesk Netfabb CAD software (San Rafael, CA, USA). Test specimens were manufactured using 3D printable experimental flexible material (Code: BM2008, GC, Tokyo, Japan). The specimens were divided according to the coil height into five groups, group A (n=4mm), group B (n=6mm), group C (n=8mm), group D (n=10mm) and group E (n=12mm). All group specimens were mechanically tested using a universal testing machine. Statistical analysis was performed using K-S-Test to compare the values of each to the control group (p< 0.001).
Results: The highest value in all groups was achieved by 5.43 N/mm in group A, while the lowest value was achieved by 0.11 N/mm in group E.
Conclusions: 3D printed springs are mechanically affected by the coil heights and there is a direct correlation to the resulting force. Furthermore, the variations within the investigated groups must be thoroughly investigated prior to clinical application.