Estudio de la resistencia a la corrosión por picadura de aceros inoxidables austeníticos: influencia de la adición de manganeso en solución sólida

• Calderón-Hernández, José Wilmar ^[1] ; Braga Luz, Lara Beatriz ^[1] ; Hincapie-Ladino, Duberney ^[1] ; Alonso-Falleiros, Neusa ^[1]
  1. [1] Universidade de São Paulo

     Universidade de São Paulo

     Brasil

     
• Localización: Revista ION: Investigación, Optimización y Nuevos Procesos en Ingeniería, ISSN-e 2145-8480, ISSN 0120-100X, Vol. 28, Nº. 1, 2015 (Ejemplar dedicado a: Revista ION), págs. 63-72
• Idioma: español
• Títulos paralelos:
  • Study of pitting corrosion resistance of austenitic stainless steels: influence of the manganese addition in solid solution
  • Estudo da resistência à corrosão por pite de aços inoxidáveis austeníticos: influência da adição de manganês em solução solida
• Enlaces
  • Texto completo
• Resumen
  • español

    Este documento presenta los resultados de una investigación sobre la influencia del Mn en solución sólida sobre la resistencia a la corrosión por picadura de dos aceros inoxidables austeníticos, uno denominado 17 Cr 6Mn 5Ni y un acero comercial UNS S304L utilizado como material de referencia. Fueron usadas soluciones electrolíticas de 0,6M NaCl en tres diferentes condiciones de concentración de oxígeno (solución desaireada, naturalmente aireada y aireada artificialmente). El desempeño de cada condición fue medido a través de ensayos de polarización potenciodinámica y mediante exámenes metalográficos. Se determinaron los potenciales de corrosión (Ecorr) y de picadura (Ep). La concentración de oxígeno en la solución electrolítica influenció el parámetro Ecorr, pero no el Ep.El manganeso en solución sólida beneficia la absorción de iones Cl- en aceros inoxidables austeníticos, ejerciendo por tanto un efecto negativo en cuanto a resistencia a corrosión por picadura. A través de datos experimentales de energía libre de Gibbs de formación de compuestos (∆G°) y de la teoría de absorción competitiva, fue propuesto un mecanismo para explicar este fenómeno.

  • English

    In this research are shown the results about the study of the influence of manganese in solid solution on the pitting corrosión resistance of austenitic stainless steels, a steel is referred to as 17Cr6Mn5Ni and the UNS S304L steel as benchmarking material. Electrolytic solution containing 0.6M NaCl in three different oxygen concentration were used (aerated, non aerated and naturally aerated). The behavior of each condition was measured through potentiodynamic polarization tests and metallographic examinations. The values of corrosion potential (Ecorr) and pitting potential (Ep) were determined. The oxygen concentration of the electrolytic solution influenced the Ecorr but not the Ep parameter.Manganese in solid solution benefits the Cl- ions absorption in austenitic stainless steels. Therefore, causes negative effect on pitting corrosion resistance. A mechanism was proposed through the standard Gibbs free energy of formation of compounds (∆G°) data, and through the competitive absorption theory.

  • português

    Este documento apresenta os resultados de uma pesquisa sobre a influencia do Mn em solução sólida sobre a resistência à corrosão por pite de aços inoxidáveis austeníticos, um denominado 17Cr6Mn5Ni e um aço comercial UNS S304L utilizado como material de referencia. Foram usadas soluções electrolíticas de 0,6M NaCl em três diferentes condições de concentração de oxigênio (solução desaerada, naturalmente aerada e aerada artificialmente). O desempenho de cada condição foi medido a través de testes de polarização potenciodinâmica e mediante exames metalográficos. Determinaram-se os potencias de corrosão (Ecorr) e de pite (Ep). A concentração de oxigênio na solução eletrolítica influenciou o parâmetro Ecorr, mas não o Ep.O manganês em solução sólida beneficia a absorção de íons Cl- em aços inoxidáveis austeníticos, exercendo, portanto um efeito negativo quanto à resistência à corrosão por pite. Através de dados experimentais de energia livre de Gibbs de formação de compostos (∆G°) e da teoria de absorção competitiva, foi proposto um mecanismo para explicar este fenômeno.