O efeito do pós-fabrico nas propriedades dos painéis de fibra de alta densidade do pinho retardado

• Autores: Idalina Domingos, Paulo Almeida, Bruno Esteves, Eduardo José Ferreira Dos Santos
• Localización: Millenium, ISSN-e 1647-662X, Serie 2, Nº. Extra 3, 2019, págs. 13-20
• Idioma: portugués
• Títulos paralelos:
  • The effect of post-manufacture on the properties of hight density fire-retardant treated fiberboard panels
  • Efecto de la frabricación de postes en las propriedades de los paneles de fiberboard de pino tratado
• Enlaces
  • Texto completo (pdf)
• Resumen
  • español

    Introducción: Las placas de aglomerado de fibras presentan grandes ventajas en la fabricación de muebles, a pesar de su inherente inflamabilidad. Este problema puede solventarse tratando los paneles con los correctos aditivos retardadores del fuego.

    Objetivos: Un conjunto de paneles de fibra de alta densidad pasaron por varias operaciones de prensado en caliente con el fin de estudiar la influencia de este procedimiento en las propiedades del sustrato.

    Métodos: El plan experimental se desarrolló para tres temperaturas distintas de 95 °C, 180 °C y 210 °C y dos tiempos de prensado diferentes (22 segundos y 35 segundos) para cada una. Los paneles estaban hechos de fibra de pino (Pinus pinaster), tenían una densidad media de 930 kg/m3 y un grosor de 6,7 mm.

    Resultados: Los resultados indicaron que el prensado en caliente post-fabricación de los paneles de alta densidad tratados con agente ignifugante llevó a una ligera mejora en el módulo de elasticidad (MOE) y en la resistencia a la flexión de los paneles utilizados como sustrato. Se observó una disminución en el contenido de humedad y en el grosor de las placas de fibra, así como un aumento de su densidad e hinchazón cuando se aplicaron a los paneles temperaturas más altas y tiempos de presión más largos De igual forma hubo también una ligera disminución de la resistencia interna de los paneles debido a la presencia del agente ignifugante que ocasionó una disminución de la capacidad de unión de la resina.

    Conclusiones: Se observó una ligera mejora en las propiedades del sustrato, excepto en la resistencia interna de los paneles que presentó una ligera disminución debido a la interferencia del agente ignifugante.

  • English

    Introduction: Fiberboard panels present great advantages in furniture manufacturing despite their inherent flammability. This problem will be solved by treating those panels with the right fire retardant (FR) additives.

    Objectives: A set of high density fiberboard went through several hot pressing operations in order to study the influence of this procedure on the substrate properties.

    Methods: The experimental plan was developed for three different temperatures of 95 °C, 180 °C and 210 °C and two different pressing times (22 seconds and 35 seconds) for each. The panels were made out of pine fibers (Pinus pinaster) and had an average density of 930 kg/m3 and were 6.7 mm thick.

    Results: The results indicated that the post-manufacture hot-pressing of the FR-treated HDF panels led to a slight improvement in the modulus of elasticity (MOE) and in the bending strength of the panels used as substrates. A decrease in the moisture content and in the fiberboards’ thickness and an increase in their density and in their thickness swelling was observed as higher temperatures and longer pressing times were applied to the panels.

    Conclusions: There was also a slight decrease in the internal bonding strength of the panels due to the presence of the flame retardant which leads to a decrease in the bonding capacity of the resin. Conclusions: There was a slight improvement in the properties of the substrate except in the fiberboards’ internal bonding strength which experienced a slight decrease due to the interference of the fire retardant.

  • português

    Introdução: As placas de aglomerado de fibras apresentam grandes vantagens na fabricação de móveis, apesar da sua inerente inflamabilidade. Este problema pode ser melhorado tratando os painéis com os corretos aditivos retardadores de fogo.

    Objetivos: Um conjunto de painéis de fibra de alta densidade passou por várias operações de prensagem a quente, a fim de estudar a influência deste procedimento nas propriedades do substrato.

    Métodos: O plano experimental foi desenvolvido para três temperaturas diferentes de 95 °C, 180 °C e 210 °C e dois tempos diferentes de prensagem (22 segundos e 35 segundos) para cada uma. Os painéis foram feitos de fibras de pinho (Pinus pinaster) e tinham uma densidade média de 930 kg / m3 e espessura de 6,7 mm.

    Resultados: Os resultados indicaram que a prensagem a quente pós-fabricação dos painéis de alta densidade tratados com agentes ignifugantes conduziu a uma ligeira melhoria no módulo de elasticidade (MOE) e na resistência à flexão dos painéis utilizados como substratos. Uma diminuição no teor de humidade e na espessura das placas de fibra e um aumento da sua densidade e inchamento foram observados quando temperaturas mais altas e tempos de prensagem mais longos foram aplicados aos painéis.

    Houve também uma ligeira diminuição da resistência interna dos painéis devido à presença do agente ignifugante que levou a uma diminuição na capacidade de ligação da resina.

    Conclusões: Houve uma ligeira melhoria nas propriedades do substrato, exceto na resistência interna dos painéis, que apresentou uma ligeira diminuição devido à interferência do agente ignifugante.