In this work, films consisting of xanthan gum (GX), carboxymethylcellulose (CMC) and GX/CMC blend were prepared in the absence and presence of citric acid as a crosslinking agent. The films were prepared by casting method and characterized in terms of their solubility in water, swelling capacity, thermal stability and soil degradation. This paper showed that citric acid can cross–link both polymers and modify the properties studied. The crosslinked films presented similar solubility in water (16–19%). Crosslinked blend presented the highest swelling degree ( 87%) and soil degradation ( 45%) and also the lower thermal stability than the other compositions. The films formed by CMC non–crosslinked presented higher thermal stability.
Neste trabalho, filmes formados por goma xantana (GX), carboximetilcelulose (CMC) e blenda GX/CMC foram preparados na ausência e na presença de ácido cítrico como agente reticulante. Os filmes foram formados pela técnica de evaporação do solvente e caracterizados através de solubilidade em água, capacidade de intumescimento, estabilidade térmica e degradação no solo. Este artigo mostrou que o ácido cítrico pode reticular ambos os polímeros e modificar as propriedades estudadas. Os filmes reticulados apresentaram similar solubilidade em água (16–19%). A blenda reticulada apresentou o maior grau de intumescimento ( 87%) e de degradação no solo ( 45%) e também a menor estabilidade térmica em relação às demais composições. O filme formado por CMC não reticulado apresentou maior estabilidade térmica.
© 2001-2024 Fundación Dialnet · Todos los derechos reservados