Comportamento viscosimétro da poliamida 66 comercial em ácido fórmico y ácido clorídrico

• Autores: Jocelei Duarte, Venina dos Santos, Mara Zeni
• Localización: Revista Iberoamericana de Polímeros, ISSN 1988-4206, ISSN-e 0121-6651, Vol. 17, Nº. 6, 2016, págs. 293-303
• Idioma: español
• Enlaces
  • Texto completo (pdf)
• Resumen
  • English

    In this study the viscosity average molecular weight (Mv) of a commercial polyamide 66 (PA66) was determined and the viscometric behavior of PA66 solutions using 90% formic acid (FA), and 37–38% hydrochloric acid (HCl) as solvents were evaluated. The measurements were performed in the Ubbelohde Viscometer at 25 ± 0.5°C, and the equations of Huggins and Kraemer were used in order to determine the intrinsic viscosity [η] for both binary systems (PA66/FA and PA66/HCl). The intrinsic viscosity values for PA66 in FA was 0.555 dL·g–1 and in HCl was 0.185 dL·g–1. The average viscometric radius (Rv) of PA66 molecule in solution is about 30% lower in HCl than when FA was employed, which may be related to the polymer–solvent interaction parameter.

  • português

    Neste trabalho foi determinado a massa molar viscosimétrica média (Mv) de uma poliamida 66 (PA66) comercial e avaliado o comportamento viscosimétrico das soluções de PA66 utilizando ácido fórmico 90% (FA) e ácido clorídrico 37–38% (HCl) como solventes. As medidas foram realizadas em viscosímetro de Ubbelohde a temperatura de 25 ± 0,5°C, e usadas as equações de Hugginse de Kraemer na determinação das viscosidades intrínsecas [η] para ambos os sistemas binários (PA66/FA e PA66/HCl). Os valores da viscosidade intrínseca encontrados para a PA66 em FA foi de 0,555 dL·g–1e em HClfoi de 0,185 dL·g–1.O raio viscosimétrico médio (RV) da molécula de PA66 em solução é aproximadamente 30% menor em HCl do que quando em FA, o que pode estar relacionado com oparâmetro de interação polímero –solvente.