Relación entre entalpías de inmersión de carbones activados modificados en su química superficial en diferentes líquidos y sus características fisicoquímicas

• Autores: Paola Rodríguez Estupiñán, Liliana Giraldo Gutiérrez, Juan Carlos Moreno Piraján
• Localización: Afinidad: Revista de química teórica y aplicada, ISSN 0001-9704, Vol. 72, Nº. 570, 2015, págs. 114-119
• Idioma: español
• Títulos paralelos:
  • Relació entre entalpies d’immersió de carbons activats modificats en la seva química superficial en diferents líquids i les seves característiques fisicoquímiques
  • Relationship between enthalpy of immersion of activated carbons modified at their surface chemistry in different liquids and their physicochemical characteristics
• Enlaces
  • Texto completo
• Dialnet Métricas: 1 Cita
• Resumen
  • español

    Se determinan entalpías de inmersión de carbones activados modificados químicamente en benceno, diclorometano, tetracloruro de carbono y agua; que presentan los valores mayores para la inmersión de los sólidos en diclorometano en un rango de -96 a -155 Jg-1 y para la inmersión en agua valores entre -32 y -66 Jg-1• Los carbones activados presentan valores de área BET y volúmenes de microporos entre 783 y 935 m29-1 y 0,31 y 0,37 cm39-1 respectivamente. Se determinaron entalpías de inmersión de los carbones activados en soluciones acuosas de Ni(ll) de 500 mgL-1• Para las entalpías de inmersión de los carbones activados en soluciones de Ni(ll) el mayor valor se obtiene para el carbón activado oxidado con ácido nítrico, de -69,2 Jg·1, que indica la influencia de la química superficial en el proceso de adsorción del ion desde solución acuosa. Se obtiene una relación directa entre la entalpía de inmersión de los sólidos en la solución y la capacidad de adsorción.

  • English

    Immersion enthalpies of chemically modified activated carbon in benzene, dichloromethane, carbon tetrachloride and water were determined which present higher values for the immersion of the solids in dichloromethane at a range of -96 to -155 Jg-1 and for immersion values in water between -32 and -66 Jg-1. Activated carbons have BET area values and micropore volumes between 783 and 935 m2g-1 and 0.31 and 0.37 cm3g-1, respectively.Immersion enthalpies of activated carbons in Ni(II) aqueous solutions of 500 mgL-1 were determined. For immersion enthalpies of activated carbons in Ni(II) solutions the highest value was obtained for the oxidized activated carbon with nitric acid, -69.2 Jg-1, indicating the influence of surface chemistry on the ion adsorption process from aqueous solution. Obtain a direct relationship between the immersion enthalpy of solids in the solution and the adsorption capacity.

  • català

    Es determinen entalpies d’immersió de carbons acti-vats modificats químicament en benzè, diclorometà, tetraclorur de carboni i aigua; que presenten els va-lors més grans per a la immersió dels sòlids en dicloro-metà en un rang de -96 a -155 Jg-1 i per a la immersió en aigua valors entre -32 i -66 Jg-1. Els carbons activats presenten valors d’àrea BET i volums de microporus en-tre 783 i 935 m2g-1 i 0,31 i 0,37 cm3g-1, respectivament. Es van determinar entalpies d’immersió dels carbons acti-vats en solucions aquoses de Ni(II) de 500 mgl-1. Per a les entalpies d’immersió dels carbons activats en solucions de Ni(II) el major valor s’obté per al carbó activat oxidat amb àcid nítric, de -69,2 Jg-1, que indica la influència de la quí-mica superficial en el procés d’adsorció de l’ió en solució aquosa. S’obté una relació directa entre l’entalpia d’immer-sió dels sòlids en la solució i la capacitat d’adsorció.