Análise topográfica de trinca de corrosão em aço AISI 304L: estudo de caso

• Autores: Jan Vatavuk, Sônia B. Faldini
• Localización: Revista Mackenzie de engenharia e computação, ISSN 1518-7470, Nº. 4, 2003-4, págs. 151-163
• Idioma: portugués
• Texto completo no disponible (Saber más ...)
• Resumen
  • English

    A general discussion about austenitic stainless stress corrosion craking phenomena is carried out concerning some topographic aspects as well as crack trajectory pattern. The presentation was conducted through a carefully scanning electron microscope fracture analysis to obtain the real topography due to the stress corrosion cracking phenomena. The analysis was conducted in the borderline between the stress corrosion cracking fracture and that produced between stress corrosion cracking surface and cleavage in ferritic stainless steel are presented and discussed in terms of topographic characteristic.

  • português

    O presente trabalho realiza uma discussão geral a respeito do fenômeno de corrosão sob tensão en aços inoxidáveis austeníticos com especial atenção no que se refere à trajetória de trinca e seus aspectos topográficos. A presentação está baseada em um estudo de caso, no cual se desenvolveu uma cuidadosa técnicade análise tropográfica em microscópio eletrônico de varredura, com o objetivo de averiguar a real topografia da trinca buscando-se imagens muito próximas das produzidas por fratura induzida propositalmente por ocasião da separação das faces de fratura. Realiza-se também uma comparação entre a superfície de fratura gerada por corrosão sob tensão na liga austenítica estudada com uma fratura por clivagem em aço inoxidável ferrítico, sempre mediante a técnica de microscopia eletrônica de varredura.