Determinação do tamanho de rede polimérica de hidrogéis à base de polivinilpirrolidona (PVP)

• Autores: Leila F. de Miranda, Ademar B. Lugão, Luci D. B. Machado, Leonardo G. Andrade e Silva
• Localización: Revista Mackenzie de engenharia e computação, ISSN 1518-7470, Nº. 1, 2000-1, págs. 81-91
• Idioma: portugués
• Texto completo no disponible (Saber más ...)
• Resumen
  • English

    The mesh size of polymer network, average molar mass, between crosslinking and swelling equilibrium degree, of the polyvynilpyrrolidone hydrogel dressing were determined. The PVP based hydrogel was prepared by radioinduced crosslinking at IPEN's electron accelerator at does of 10 to 100kGy and PVP concentration of 2 to 16%. The exprimental results showed that the mesh size of polymer network and the average molar mass, between crosslinking and swelling equilibrium degree, decrease with the increase with both PVP concentration and radiation dose.

    It was also observer that the doses effect has more influence that PVP concentration.

  • português

    Neste trabalho foram determinados o tamanho da rede polimérica, massa molar média, entre as ligações cruzadas e o grau de intumescimento do curativos de hidrogéis de polivinilpirrolidona. Os hidrogéis à base de PVP foram preparados por ligaçoes cruzadas radioinduzidas no acelerador de eléctrons do IPEN nas doses de 10 a 100kGy e concentrações de PVP de 2 a 16%.

    Os resultados experimentais mostraram que o tamanho da rede polimérica e a massa molar média, entre as ligações cruzadas e o grau de inmescimento no equilíbrio, decrescem com a concentração de PVP e a dose de radiação. Também se observou que o efeito da dose tem mais influência que a concentração de PVP.