Algumas observações sobre o aspecto macroscópico das falhas em fadiga torsional reversa

• Autores: J. Stryhalski, Renato Barbieri
• Localización: Revista iberoamericana de ingeniería mecánica, ISSN 1137-2729, Vol. 18, Nº 2, 2014, págs. 113-124
• Idioma: portugués
• Enlaces
  • Texto completo
• Resumen
  • English

    This article reports the study of torsional fatigue reverse, R =- 1, and the failure modes and crack propagation for Steel SAE 1020 hot-drawn , Aluminum and Cast Iron Gray6063, in the literature is that the patterns of failure always are combinations of modes I, Mode II and Mode III. In th is document is given the curve of fatigue specimens in the shape of an hourglass.

    It also investigates the patterns of failure from the beginning of macroscopic crack untilthe final rupture of the specimen. Noting that in most cases the crack starts in Mode II, with further branch to the Mode I to failure at high cycles, and branch to the Mode III for medium and low cycle.

  • português

    Este artigo relata o estudo de fadiga torsional reversa, R =-1 , e os modos de falha e propagação de trinca para Aço SAE 1020 trefilado a quente, Alum ínio 6063 e Ferro Fundido Cinzento, na literatura encontram-se que os padrões de falha sempre são combinações dos Modos I, Modo II e Modo III. É determinada a curva de fadiga de corpos de prova com a forma de uma ampulheta. Também investigam-se os padrões de falha macroscópicos desde o início da trin ca até a ruptura final do corpo de prova. Verificando-se que na maioria dos casos a trinca inicia no Modo II, co m posterior ramificação para o Modo I até a falha em altos ciclos, e ramificação para o Modo III para médio e baixo ciclo