Efecto de la temperatura del electrolito sobre la resistencia a corrosión de recubrimientos de nitruro de cromo, cromo duro y pinturas tipo epoxy

• Autores: Magda Marcela Torres Luque, John Jairo Olaya Flórez
• Localización: Ingeniería y universidad, ISSN 0123-2126, Vol. 17, Nº. 1, 2013, págs. 109-125
• Idioma: español
• Títulos paralelos:
  • Efeito da temperatura do eletrólito sobre a resistência à corrosão de revestimentos de nitreto de cromo, cromo duro e tintas do tipo epoxy
  • Effects of Electrolyte Temperature on the Corrosion Resistance of Chromium Nitride, Hard Chromium and Epoxy Paint Coatings
• Enlaces
  • Texto completo (pdf)
• Resumen
  • español

    En este trabajo se compara la influencia de la temperatura del electrolito en la resistencia a la corrosión de recubrimientos cerámicos de nitruro de cromo (CrN) producidos con el sistema de sputtering con magnetrón desbalanceado (UBM) con recubrimientos metálicos industriales de cromo duro y pinturas orgánicas tipo epoxy. Todos los recubrimientos se depositaron sobre aceros al carbono A36. La evaluación de la resistencia a la corrosión se determinó mediante ensayos de espectroscopia de impedancia electroquímica (EIS) en una solución al 3 % de cloruro de sodio.

    Para ello se varió la temperatura del electrolito desde 20 ºC hasta 80 ºC, y viceversa, con un paso de 20 ºC y tomando mediciones cada 24 h. En general, los recubrimientos orgánicos presentaron la menor degradación con el tiempo de ensayo; sin embargo, al finalizar el ciclo de temperatura, la resistencia a la corrosión fue similar en los recubrimientos orgánicos y cerámicos. En esta investigación se discuten los mecanismos de corrosión para los recubrimientos producidos.

  • English

    This paper compares the influence of the temperature of the electrolyte in corrosion resistance of ceramic coatings of Chromium Nitride (CrN) produced with the unbalanced magnetron sputtering system (UBM) with industrial metallic coatings of hard chromium and organic epoxy paints. All coatings were deposited over A36 carbon steel. The evaluation of corrosion resistance was determined through electrochemical impedance spectroscopy (EIS) in a 3% sodium chloride solution. For this purpose the temperature of the electrolyte was varied from 20 ºC to 80 ºC, and vice versa, with an interval of 20 ºC and taking measures every 24 hours. In general, organic coatings presented the least degradation in the time of the experiment; nevertheless, by the time the temperature cycle was over, the corrosion resistance was similar in the organic coatings and the ceramic ones. This paper discusses the corrosion mechanisms for each of the coatings produced.

  • português

    Este trabalho compara a influencia da temperatura do eletrolito na resistencia a corrosao de revestimentos ceramicos de nitreto de cromo (CrN) produzidos com o sistema de sputtering com magnetron desbalanceado (UBM) com revestimentos metalicos industriais de cromo duro e tintas organicas do tipo epoxy. Todos os revestimentos depositaram-se sobre acos de carbono A#6. A avaliacao da resistencia a corrosao foi determinada mediante experimentos de espectroscopia de impedancia eletroquimica (EIS) em uma solucao de 3% de cloreto de sodio.

    Para isso, variou-se a temperatura do eletrolito de 20 ¢ªC a 80 ¨¬C, e viceversa, com passagens regulares de 20 ¨¬C, fazendo as medicoes a cada 24 h. Em geral, os revestimentos organicos apresentaram a menor degradacao durante o tempo do experimento; no entanto, ao finalizar o ciclo de temperatura, a resistencia a corrosao foi similar nos revestimentos organicos e ceramicos.

    Na presente pesquisa, discutem-se os mecanismos de corrosao dos revestimentos produzidos.