Design of a cementitious material with Nopal Mucilage and PET aggregates to improve the electrochemical properties of concrete.

• Menchaca Campos, Elsa Carmina ^[1] ; Diaz Blanco, Yohandry ^[1] ; Rocabruno Valdes, Carolin Ivette ^[1] ; Tamayo Aguilar, Yonger ^[1] ; Flores Nicolas, Alejandro ^[2] ; Uruchurtu Chavarin, Jorge ^[1]
  1. [1] Universidad Autónoma del Estado de Morelos

     Universidad Autónoma del Estado de Morelos

     México

     
  2. [2] Universidad Autónoma de Baja California

     Universidad Autónoma de Baja California

     México

     
• Localización: ALCONPAT, ISSN-e 2007-6835, Vol. 16, Nº. 2, 2026 (Ejemplar dedicado a: Volume 16, Issue 2 (2026); i - ii), págs. 200-220
• Idioma: inglés
• Títulos paralelos:
  • Projeto de um material cimentício com mucilagem nopal e agregados PET para melhorar as propriedades eletroquímicas do concreto armado.
  • Diseño de un material cementicio con mucílago de nopal y agregados de PET para mejorar las propiedades electroquímicas del concreto reforzado.
• Enlaces
  • Texto completo (pdf)
• Resumen
  • español

    Este trabajo se centró en el estudio del concreto reforzado (RC) con la adición de mucílago de nopal (NM) y polietilen tereftalato (PET). Se prepararon muestras con diferentes geometrías de PET: partículas (P), mezcla de fibras largas y partículas (LF-P), y fibras cortas (SF) combinadas con NM. Las muestras se evaluaron mediante potencial de media-celda (HCP), ruido electroquímico (EN) y resistencia a la polarización lineal (LPR). Los valores de resistencia a la compresión (f'c.) disminuyeron con la adición de PET. Las muestras con PET y NM obtuvieron valores más bajos de velocidad de corrosión (Icorr). El diseño de PET y el almacenamiento de NM pueden ser un desafío de analizar. Ambos materiales aportaron propiedades que aumentaron la durabilidad del RC.

  • English

    This work focused on the study of reinforced concrete (RC) with the addition of nopal mucilage (NM) and (polyethylene terephthalate) PET aggregates. Samples were prepared with different PET geometries: particles (P), a mixture of long fibers and particles (LF-P), and short fibers (SF) combined with NM. Samples were evaluated using half-cell potential (HCP), electrochemical noise (EN), and linear polarization resistance (LPR). A decrease in compressive strength (f'c.) values was observed with increasing PET percentage. Samples with PET and NM achieved lower values of corrosion rate (Icorr). PET design and storing the NM can be a challenge to analyze. Both materials contributed to increased the durability of RC.

  • português

    Este trabalho teve como foco o estudo do concreto armado (RC) com adição de mucilagem de nopal (NM) e agregados de tereftalato de polietileno (PET). Foram preparadas amostras com diferentes geometrias de PET: partículas (P), mistura de fibras longas e partículas (LF-P) e fibras curtas (SF), combinadas com NM. As amostras foram avaliadas por meio de potencial de meia-célula (HCP), ruído eletroquímico (EN) e resistência à polarização linear (LPR). Os valores de resistência à compressão (f'c.) diminuíram com a adição de PET. As amostras com PET e NM apresentaram menores valores de velocidade de corrosão (Icorr). A configuração geométrica do PET e o armazenamento da NM podem representar desafios analíticos. Ambos os materiais contribuíram para aumentar a durabilidade do concreto armado.