Resistencia a la compresión de conectores con diferentes áreas en prótesis parciales fijas de tres zirconias monolíticas policromáticas

Williams Gregory Gomez Pacheco; Adriana Echevarria-Goche; Arturo Kobayashi Shinya; Gustavo Augusto Huertas Mogollón

Ayuda

Resistencia a la compresión de conectores con diferentes áreas en prótesis parciales fijas de tres zirconias monolíticas policromáticas

Gomez Pacheco, Williams Gregory ^[1] ; Echevarria-Goche, Adriana ^[2] ; Kobayashi Shinya, Arturo ^[2] ; Huertas Mogollón, Gustavo ^[1]
1. [1] Universidad Científica del Sur
  
  Universidad Científica del Sur
  
  Perú
2. [2] Universidad Peruana Cayetano Heredia
  
  Universidad Peruana Cayetano Heredia
  
  Perú
Localización: Revista Estomatológica Herediana, ISSN-e 2225-7616, Vol. 36, Nº. 1, 2026 (Ejemplar dedicado a: Enero-marzo; e6640)
Idioma: español
Títulos paralelos:
- Resistência à compressão de conectores com diferentes áreas em próteses parciais fixas de três zircônias monolíticas policromáticas
- Compressive strength of connectors with different areas in three-unit polychromatic monolithic zirconia fixed partial dentures
Enlaces
- Texto completo
Resumen
- español
  Objetivo: Comparar la resistencia a la compresión de conectores con distintas áreas en prótesis parciales fijas (PPF) de tres unidades, confeccionadas con tres tipos de zirconia monolítica policromática mediante tecnología CAD/CAM. Materiales y métodos: Se realizó un estudio experimental in vitro con 30 muestras de PPF confeccionadas con tres marcas de zirconias monolíticas policromáticas: IPS e.max® ZirCAD MT Multi (Ivoclar Vivadent; Schaan, Liechtenstein), KatanaTM Zirconia Super Translucent Multi Layered (STML) (Noritake Dental Supply; Okayama, Japón) y Ceramill® Zolid fx Multilayer (Amann Girrbach; Koblach, Austria). Para cada marca se confeccionaron 10 especímenes, subdivididos en dos subgrupos según el área del conector: 9 mm2 (n = 5) y 12 mm2 (n = 5). Los especímenes fueron sometidos a pruebas de resistencia a la compresión en una máquina de ensayos universales (CMT-5L, LG; Anyang, Corea del Sur), aplicando una carga vertical en el centro del póntico hasta la fractura. Los datos obtenidos se analizaron mediante las pruebas de Kruskal-Wallis y U de Mann-Whitney. Resultados: Los conectores de 12 mm2 mostraron una resistencia a la compresión significativamente mayor que los conectores de 9 mm2, independientemente de la marca utilizada, con medianas de 1557,76 N (RIC: 425,54 N) frente a 1180,40 N (RIC: 705,32 N), respectivamente (p = 0,024). Las zirconias KatanaTM Zirconia STML e IPS e.max® ZirCAD MT Multi alcanzaron valores de resistencia superiores a las de Ceramill® Zolid fx Multilayer en ambos tamaños de conector (p < 0,05). Conclusiones: El área del conector influyó significativamente en la resistencia a la compresión de las PPF de zirconia monolítica policromática. Los conectores de 12 mm2 presentaron mayor resistencia, y las marcas KatanaTM Zirconia STML e IPS e.max® ZirCAD MT Multi mostraron un mejor desempeño en comparación con Ceramill® Zolid fx Multilayer. Estos hallazgos sugieren que el incremento del área del conector favorece la longevidad clínica de las restauraciones.
- English
  Objective: To compare the compressive strength of connectors with different areas in three-unit fixed partial dentures (FPDs) fabricated from three types of polychromatic monolithic zirconia using CAD/CAM technology. Materials and methods: An in vitro experimental study was conducted with 30 FPD samples fabricated from three brands of polychromatic monolithic zirconia: IPS e.max® ZirCAD MT Multi (Ivoclar Vivadent; Schaan, Liechtenstein), KatanaTM Zirconia Super Translucent Multi Layered (STML) (Noritake Dental Supply; Okayama, Japan), and Ceramill® Zolid fx Multilayer (Amann Girrbach; Koblach, Austria). For each brand, 10 specimens were fabricated and subdivided into two subgroups according to connector area: 9 mm² (n = 5) and 12 mm² (n = 5). The specimens were subjected to compressive strength testing in a universal testing machine (CMT-5L, LG; Anyang, South Korea), applying a vertical load at the center of the pontic until fracture occurred. The obtained data were analyzed using the Kruskal -Wallis and Mann -Whitney U tests. Results: The 12 mm² connectors showed significantly greater compressive strength than the 9 mm² connectors, regardless of the brand used (medians of 1557.76 N [IQR: 425.54 N] vs. 1180.40 N [IQR: 708.32 N]; p = 0.024). KatanaTM Zirconia STML and IPS e.max® ZirCAD MT Multi zirconia achieved higher strength values than Ceramill® Zolid fx Multilayer for both connector sizes (p < 0.05). Conclusions: Connector area significantly influenced the compressive strength of polychromatic monolithic zirconia FPDs. The 12 mm² connectors exhibited greater strength, and KatanaTM Zirconia STML and IPS e.max® ZirCAD MT Multi showed better performance compared with Ceramill® Zolid fx Multilayer. These findings suggest that increasing connector area may favor the clinical longevity of restorations.
- português
  Objetivo: Comparar a resistência à compressão de conectores com diferentes áreas em próteses parciais fixas (PPF) de três unidades, confeccionadas com três tipos de zircônia monolítica policromática por meio da tecnologia CAD/CAM. Materiais e métodos: Foi realizado um estudo experimental in vitro com 30 amostras de PPF confeccionadas com três marcas de zircônia monolítica policromática: IPS e.max® ZirCAD MT Multi (Ivoclar Vivadent; Schaan, Liechtenstein), Katana TM Zirconia Super Translucent Multi Layered (STML) (Noritake Dental Supply; Okayama, Japão) e Ceramill® Zolid fx Multilayer (Amann Girrbach; Koblach, Áustria). Para cada marca foram confeccionados 10 espécimes, subdivididos em dois subgrupos de acordo com a área do conector: 9 mm² (n = 5) e 12 mm² (n = 5). Os espécimes foram submetidos a testes de resistência à compressão em uma máquina universal de ensaios (CMT-5L, LG; Anyang, Coreia do Sul), aplicando-se uma carga vertical no centro do pôntico até ocorrer a fratura. Os dados obtidos foram analisados por meio dos testes de Kruskal -Wallis e U de Mann -Whitney. Resultados: Os conectores de 12 mm² apresentaram resistência à compressão significativamente maior do que os conectores de 9 mm², independentemente da marca utilizada (medianas de 1557,76 N [RIQ: 425,54 N] versus 1180,40 N [RIQ: 708,32 N]; p = 0,024). As zircônias Katana TM Zirconia STML e IPS e.max® ZirCAD MT Multi alcançaram valores de resistência superiores aos da Ceramill® Zolid fx Multilayer em ambos os tamanhos de conector (p < 0,05). Conclusões: A área do conector influenciou significativamente a resistência à compressão das PPF de zircônia monolítica policromática. Os conectores de 12 mm² apresentaram maior resistência, e as marcas Katana TM Zirconia STML e IPS e.max® ZirCAD MT Multi demonstraram melhor desempenho em comparação com Ceramill® Zolid fx Multilayer. Esses achados sugerem que o aumento da área do conector pode favorecer a longevidade clínica das restaurações.