Comparing Dry and Wet High-Intensity Magnetic Separation for Iron Removal from Low-Grade Magnesite Ore

• Mohammed S. Alhaddad ^[1] ; Hussin A. M. Ahmed ^[1]
  1. [1] King Abdulaziz University

     King Abdulaziz University

     Arabia Saudí

     
• Localización: Afinidad: Revista de química teórica y aplicada, ISSN 0001-9704, Vol. 82, Nº. 605, 2025, págs. 351-358
• Idioma: inglés
• Títulos paralelos:
  • Comparació de la separació magnètica d’alta intensitat seca i humida per a l’eliminació del ferro del mineral de magnesita de baix grau
  • Comparación de la separación magnética de alta intensidad seca y húmeda para la eliminación de hierro de mineral de magnesita de bajo grado
• Enlaces
  • Texto completo
• Resumen
  • español

    Este artículo investiga la eliminación de impurezas de hierro de un mineral de magnesita saudita de baja ley (37,68% MgO y 1,91% Fe2O3). Se exploraron técni-cas de separación magnética de alta intensidad tanto húmedas como secas. En la separación magnética seca utilizando un rodillo magnético inducido por Outotec, se optimizaron el tamaño de alimentación, la velocidad de alimentación, el campo magnético y la velocidad del rodillo. Por otro lado, utilizando un separador mag-nético húmedo de laboratorio WHIMS, los paráme-tros estudiados fueron el caudal de la pulpa, el campo magnético y la densidad de la pulpa. Los resultados muestran que se puede lograr una eliminación máxi-ma de hierro del 72,32% utilizando DHIMS (producto con 0,71% de Fe2O3 con un tamaño de alimentación (-0,212+0,05 mm), velocidad de alimentación de 0,3 kg/min, 14 kgauss y una velocidad de rodillo de 50 rpm. Sin embargo, las condiciones óptimas para la separación magnética húmeda fueron un campo magnético de 14 kgauss, 15% en peso de alimentación sólida y un caudal de . 0,4 L/min, dando como resultado un producto que tiene 0,46% Fe2O3 lo que significa una remoción de hierro del 84,25%. El producto puede ser utilizado en materiales refractarios, forros de frenos, tratamiento de cuero y soldadura. y tratamiento de aguas residuales, tratamiento de gases de combustión y pesticidas.

  • English

    This paper investigates the removal of iron impurities from a low-grade Saudi magnesite ore (37.68% MgO and 1.91% Fe2O3). Both wet and dry high-intensity magnetic separation techniques were explored. In dry magnetic separation using an Outotec-induced roll magnetic, the feed size, feed rate, magnetic field, and roll speed were optimized. On the other hand, using a WHIMS laboratory wet high magnetic separator, the studied parameters were slurry flow rate, magnetic field, and pulp density. The results show that a maximum iron removal of 72.32% can be achieved using DHIMS (product with 0.71% Fe2O3 at (-0.212+0.05 mm) feed size, 0.3 kg/min feed rate, 14 KGauss, and a roll speed of 50 rpm. However, the optimal conditions for wet magnetic separation were magnetic field of 14 KGauss, 15 wt.% solid feed, and flow rate of 0.4 L/min, lead to a product that has 0.46% Fe2O3 which mean an iron removal of 84.25%. The product can be used in refractory materi-als, brake lining, leather treatment, and welding. It is also suitable for chemical, fertilizer, and wastewater treatment, flue gas treatment, and pesticides.

  • català

    Aquest article investiga l’eliminació d’impureses de ferro d’un mineral de magnesita saudita de baix grau (37,68% MgO i 1,91% Fe2O3). Es van explorar tècniques de separació magnètica d’alta intensitat tant humida com seca. En la separació magnètica en sec mitjançant un magnètic de rotlle induït per Outotec, es van opti-mitzar la mida d’alimentació, la velocitat d’alimenta-ció, el camp magnètic i la velocitat del rotllo. D’altra banda, utilitzant un separador magnètic alt humit de laboratori WHIMS, els paràmetres estudiats van ser el cabal de purins, el camp magnètic i la densitat de la polpa. Els resultats mostren que es pot aconseguir una eliminació màxima de ferro del 72,32% utilitzant DHIMS (producte amb 0,71% de Fe2O3 a (-0,212 + 0,05 mm) mida d’alimentació, velocitat d’alimentació de 0,3 kg/min, 14 KGauss i una velocitat de rotllo de 50 rpm. Tanmateix, les condicions òptimes per a la separació magnètica humida eren un camp magnètic de 14 KGauss, 15 % en pes d’alimentació sòlida i un cabal de 0,4 L/min, donen lloc a un producte que té un 0,46% de Fe2O3, la qual cosa significa una eliminació de ferro del 84,25%. També és adequat per al tractament de productes químics, fertilitzants i aigües residuals, tractament de gasos de combustió i pesticides.